    摘要:

    研究采油过程中CT80油管与电缆在0.01~0.13 m/s速度下对摩时的摩擦磨损行为及其对油管剩余强度的影响。采用扫描电子显微镜及金相显微镜对油管组织、磨损表面及截面特征进行表征。结果表明:CT80油管的磨损量、壁厚减薄量与摩擦因数随摩擦速度增加先增大,速度达到0.07 m/s后趋于平稳;磨损率随着摩擦速度增加先增大后降低,最大磨损率对应的摩擦速度为0.07 m/s;采油过程中磨粒磨损与腐蚀磨损共同作用于油管,随着摩擦速度升高磨粒磨损造成的损失降低,腐蚀磨损造成的损失升高;随着摩擦速度增加油管的剩余抗挤毁强度以及剩余抗内压强度先降低后趋于平稳。

    Abstract:

    The influence of velocity(from 0.01 m/s to 0.13 m/s) on friction and wear behavior and the residual strength of the CT80 tubing during oil recovery were studied.The tubing microstructure and the characteristics of the wear surfaces and cross sections were analyzed by the scanning electron microscope (SEM) and the metallographic microscope.The results show that the wear mass loss and wall thickness reduction of CT80 tubing and the friction coefficient between tubing and cable are increased rapidly with increasing of friction velocity,then are stabilized when the friction velocity reaches 0.07 m/s.The wear rate of the tubing is increased first and then decreased,and the critical velocity corresponding to the maximum wear rate is 0.07 m/s.Abrasive wear and corrosive wear of the tubing occur at the same time during oil recovery,and as friction velocity increases,the wear mass loss produced by abrasive wear is decreased,while the wear mass loss produced by corrosive wear is increased.As friction velocity increases,the collapsing strength and residual internal pressure strength of the tubing are decreased first then stabilized.

    参考文献
    相似文献
    引证文献
引用本文

徐学利,王涛,余晗,董会,李霄.低摩擦速度下CT80油管摩擦磨损性能[J].润滑与密封,2019,44(2):66-71.
. Friction and Wear Properties of CT80 Tubing under Low Friction Velocity[J]. Lubrication Engineering,2019,44(2):66-71.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2019-07-04
  • 出版日期: