  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    以不锈钢为金属芯板,氟橡胶为橡胶涂层,制备出氟橡胶/不锈钢复合密封板。采用电化学测试技术(交流阻抗、极化曲线和线性扫描)对复合板进行耐蚀性能研究,通过压缩回弹实验研究复合板的密封性能。电化学测试结果表明,制备的复合板具有良好的耐蚀性能,其腐蚀电流密度为1.318 μA/cm2,极化电阻为5.93×104 Ω,传荷电阻为1.389×104 Ω/cm2。压缩回弹实验表明,该复合板压缩率为15.38%、回弹率为89.5%,密封性能优秀。

    Abstract:

    Fluorine rubber/metal composite board was prepared, which is composed of metal core board(stainless steel) and rubber coating(fluorine rubber), electrochemical method, such as AC impedance, polarization curve and liner scanning curve was used to demonstrate its corrosion resistance, and compressibility and recovery experiment was used to evaluate its sealing performance. The test result of electrochemical method shows that the prepared composite board has superior corrosion resistance, its corrosion current density is 1.318 μA/cm2, polarization resistance is 5.93×104 Ω, and charge transfer resistance is 1.389×104 Ω/cm2.The test results of compressibility and recovery experiment shows that the prepared composite board has superior sealing performance, its compressibility is 15.38%, recovery is 89.5%.

    参考文献
    相似文献
    引证文献
引用本文

张爱玲,曹 春,吕震乾,赵 超,郭婷婷,张宗成.氟橡胶/不锈钢复合板的制备及耐蚀密封性能研究[J].润滑与密封,2014,39(11):47-50.
.[J]. Lubrication Engineering,2014,39(11):47-50.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2015-04-21
  • 出版日期: