In this paper,technical parameters were optimized by using orthogonal test.Onestep hot press molding technology was used to fabricate the low reinbased brake pads.Kinds of analytical testing equipment were employed to measure the friction and wear properties and the mechanical and physical properties.The influence on properties of technical parameters was studied by the orthogonal analysis.Worn surfaces and dust were observed by microscopic analysis.The results showed that the friction coefficient was drastic influenced by hotpressing temperature.Sample using 160 ℃ hot pressing temperature had higher friction coefficient.The wear rate was greatest affected by curing time.Sample using 11 hours curing time had lower wear rate.Hardness was greatest affected by pressure.Sample using 22 MPa pressure had greater hardness.The shear strength was influenced by pressing temperature pressing temperature and curing time.Within a certain range,the shear strength was improved by longer curing time and higher hotpressing temperature.