Abstract:The nanoSiC powders with different thickness were coated on the surface of the plasmacoated FeWC cermet coating,then the coating with different nanoSiC content was prepared by using laser remelting process.The metallographic organization,microstructure and phase composition of the coating were studied by means of metallographic microscope,scanning electron microscopy (SEM) and Xray diffraction (XRD).The microhardness of the surface and cross section of the coating was measured by microhardness tester.The wear resistance was studied on the MMG10 friction and wear testing machine.The results show that with the increase of nanoSiC content,the degree of grain refinement of the coating is improved,the porosity is decreased,and the hard phases such as CrSi2 and Cr7C2 are increased in the coating,and the new phase (Fe2Si,CrSi) is also increased.The microhardness and wear resistance of the coating are also increased with the increase of nanoSiC content.